TiAl alloy was electrochemically anodized in ethylene glycol electrolyte containing with NH4F to prepare anodic film. The influence of anodization treatment on the oxidation behavior and mechanical properties of the anodized TiAl alloy were then characterized. Results shown that based on the halogen effect a continuous and dense Al2O3 oxide scale will generate on the anodized TiAl alloy after high temperature oxidation. After oxidation at 1000 ℃ for 100 h, the weight gain of the anodized TiAl alloy was dramatically decreased from 85.86 mg/cm2 to 0.67 mg/cm2. Moreover, it is shown that the surface hardness and elastic modulus of the anodized TiAl alloy decreased first and then increased with the prolonging of oxidation time. Meanwhile, the friction coefficient of the anodized TiAl alloy increased comparing to the bare TiAl alloy. The surface wear resistance of the anodized TiAl alloy exhibited similar phenomena. This is because that during high temperature oxidation process, aluminum fluorides selectively transport to the surface through pores or micro-cracks, and are oxidized to Al2O3 at the surface region. The influence of anodization treatment on the mechanical properties of the anodized TiAl alloy is attributed to the Al2O3 content contained in the oxide scale.


    Access

    Download


    Export, share and cite



    Title :

    Effect of the anodization on high tempreture oxidation behavior and mechanical properties of TiAl alloy


    Contributors:
    BAO Yating (author) / WANG Yanan (author) / ZHENG Lei (author) / LIN Xiangjun (author) / HOU Guangya (author) / TANG Yiping (author) / WU Liankui (author)


    Publication date :

    2021




    Type of media :

    Article (Journal)


    Type of material :

    Electronic Resource


    Language :

    Unknown




    Aluminum alloy anodization

    COCHIEN ELLIE L / HUSSAIN KHALID / EVANS EDWARD BENEDICT | European Patent Office | 2017

    Free access

    ALUMINUM ALLOY ANODIZATION

    COCHIEN ELLIE L / HUSSAIN KHALID / EVANS EDWARD BENEDICT | European Patent Office | 2016

    Free access

    Oxidation behavior of TiAl at high temperatures in purified oxygen

    Taniguchi, S. / Shibata, T. / Itoh, S. | Tema Archive | 1991


    Effects of Si on high temperature oxidation resistance of TiAl alloy

    Weihao, X. / Liang, Z. / Huiren, J. | British Library Online Contents | 2006


    High Temperature Mechanical Constitutive Modeling of a High-Nb TiAl Alloy

    DONG Chengli / YU Huichen / JIAO Zehui et al. | DOAJ | 2018

    Free access