After over two years service in the 'snow belt', class 12.8 bolts in GM 'A' car rear suspensions began to fail, leading to the recall of 6.4 million cars. Analysis of the failures showed that the cause was corrosion induced hydrogen assisted cracking. The long delay before failure resulted from a decarburized surface through which corrosion had to penetrate before a crack could propagate. The fracture morphology of the field failures was duplicated in laboratory salt spray tests. This type of testing also showed that hardness was the principal factor affecting durability in a corrosive environment. (Wassmann)


    Access

    Access via TIB

    Check availability in my library


    Export, share and cite



    Title :

    Delayed fracture of class 12.8 bolts in automotive rear suspensions


    Additional title:

    Verspaeteter Bruch von Bolzen der Gueteklasse 12.8 in Hinterradaufhaengungen von Automobilen


    Contributors:

    Published in:

    Publication date :

    1982


    Size :

    6 Seiten, 7 Bilder, 6 Quellen


    Type of media :

    Conference paper


    Type of material :

    Print


    Language :

    English




    Delayed Fracture of Class 12.8 Bolts in Automotive Rear Suspensions

    Hughel,T.J. / General Motors Res.Lab.,Metall.Dep.,US | Automotive engineering | 1982



    The 12.8 Hp. Delage

    Engineering Index Backfile | 1923



    REAR AUTOMOTIVE LIGHT

    DENEKA MAREK / GALEZIOWSKI KONRAD / WOJTUSIK JACEK | European Patent Office | 2020

    Free access