High cycle fatigue properties of Alloy 718 for space use were investigated at temperature range from 77 to 873 K. The testing specimens were cut from welded joints as well as the base metals. The relationship between stress amplitude and fatigue life (S-N-curve) had two steps for all the specimens at any temperatures, since the fracture mechanisms were different between low and high cycle regions. In low-cycle region, the origin of the fatigue fracture was the specimen surfaces, while in high-cycle region it was the facets inside or near the surface. And the fatigue strength depended on the austenitic grain size in high-cycle region. The facets, the origin of the fatigue fracture, corresponded to the grain size.


    Access

    Access via TIB

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    High-cycle fatigue properties of alloy 718 for space use


    Additional title:

    Ermüdungseigenschaften bei hohen Lastspielzahlen einer Legierung 718 für Raumfahrtanwendungen
    Titel japanisch


    Contributors:

    Published in:

    Publication date :

    2004


    Size :

    3 Seiten, 4 Bilder, 6 Quellen




    Type of media :

    Article (Journal)


    Type of material :

    Print


    Language :

    Japanese




    Very High Cycle Fatigue Behavior of TA11 Titanium Alloy

    JIAO Zehui / YU Huichen / ZHONG Bin et al. | DOAJ | 2017

    Free access

    High Temperature Low Cycle Fatigue Properties and Failure Mechanism of a TiAl Alloy

    DONG Chengli / YU Huichen / JIAO Zehui et al. | DOAJ | 2017

    Free access

    High-Cycle Fatigue Properties of a Titanium Alloy at Cryogenic Temperatures (AAS 03-417)

    Ogata, T. / Matsuoka, S. / American Astronautical Society | British Library Conference Proceedings | 2004


    FATIGUE CRACKING MECHANISMS OF TITANIUM ALLOY VT3-1 IN VERY-HIGH-CYCLE-FATIGUE REGIME

    A. A. Shanyavskiy / C. Bathia / A. D. Nikitin et al. | DOAJ | 2016

    Free access