As steel manufacturing processes have developed, the introduction of accelerated cooling after controlled lamination or a thermo-mechanically controlled process (TMCP) has facilitated the production of pipeline steels that offer greater resistance. The prevailing tendency is to use steels with a minimum yield strength limit of 551 MPa, as is the case with API 5L-X80 steel. The present work refers to the characterization of the mechanical properties of API 5L-X80 pipeline joints welded with self-shielded flux-cored wire. This process was evaluated under preheating conditions, with a uniform and steady heat input. All joints were welded in a flat position (IG), with the pipe turning and the torch still. Tube dimensions were 762 mm in external diameter and 16 mm in thickness. Welds were applied on single V-groove, with six weld beads, along with three levels of preheating temperatures (room temperature, 100 deg C and 160 deg C). These temperatures were maintained as the interpass temperature. The filler metal E71T8-K6, whose mechanical properties differ from those of the parent metal, was used in undermatched conditions. The weld characterization is presented according to the mechanical test results for tensile strength, hardness and impact testing. These tests were conducted according to API 1104, AWS and ASTM standards. API 1104 and API 5L standards were used as screening criteria. Based upon the results obtained, it was possible to note that it is appropriate to weld API 5L-X80 steel piping with self-shielded flux-cored wire, in conformance with API standards and with no need to use a preheating temperature.


    Access

    Access via TIB

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    Influence of preheating on API 5L-X80 pipeline joint welding with self-shielded flux-cored wire


    Contributors:
    Cooper, R. (author) / Silva, J.H.F. (author) / Trevisan, R.E. (author)

    Published in:

    Welding International ; 19 , 11 ; 882-887


    Publication date :

    2005


    Size :

    6 Seiten, 8 Bilder, 5 Tabellen, 22 Quellen




    Type of media :

    Article (Journal)


    Type of material :

    Print


    Language :

    English




    Self-Shielded Flux Cored Wire Evaluation

    T. E. Bahlow / A. W. Johnson | NTIS | 1980




    Production welding of cast irons with flux-cored wire

    Conaway,H.R. / Huntington Alloys,US | Automotive engineering | 1976


    Production Welding of Cast Irons With Flux-Cored Wire

    Conaway, Harold R. | SAE Technical Papers | 1976