It is well recognized that the use of mineral admixtures such as silica fume enhances the strength and durability of concrete. This research compares the effects of adding silica fume and nanosilica to concrete and provides a better understanding of the changes in the concrete nanostructure. Nanoindentation with scanning probe microscopy imaging was used to measure the local mechanical properties of cement pastes with 0% and 15% replacement of cement with silica fume. A reduction in the volume fraction of calcium hydroxide in a sample with silica fume provides evidence of pozzolanic reaction. Furthermore, replacing 15% cement by silica fume increased the volume fraction of the high-stiffness calcium silicate hydrate (C-S-H) by a small percentage that was comparable with the decrease in the volume fraction of calcium hydroxide. A parallel study of cement pastes with nanosilica showed that nanosilica significantly improves durability of concrete. This research provides insight into the effects of nanosilica on cement paste nanostructure and explains its effect on durability of concrete. The nanoindentation study showed that the volume fraction of the high-stiffness C-S-H gel increased significantly with addition of nanosilica. Nanoindentation results of cement paste samples with similar percentages of silica fume and nanosilica were compared. Samples with nanosilica had almost twice the amount of high-stiffness C-S-H as the samples with silica fume.


    Access

    Download

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    Comparative Study of the Effects of Microsilica and Nanosilica in Concrete


    Additional title:

    Transportation Research Record: Journal of the Transportation Research Board


    Contributors:


    Publication date :

    2010-01-01




    Type of media :

    Article (Journal)


    Type of material :

    Electronic Resource


    Language :

    English





    Shrinkage of Latex-Modified and Microsilica Concrete Overlays

    Buchanan, Patricia M. | Online Contents | 2003


    Shrinkage of Latex-Modified and Microsilica Concrete Overlays

    Buchanan, Patricia M. / Mokarem, David W. / Weyers, Richard E. et al. | Transportation Research Record | 2003