Thin PZT film is being developed for use in microelectronics, electromechanical and optoelectronic applications. Thin Pb(ZrTi)O/sub 3/ film capacitor devices were fabricated using RF sputtering techniques. The multiple-layer configuration of Si/SiO/sub 2//Ti/Pt was used as the substrate and bottom electrode. The top electrode was Pt. At 1 kHz, the dissipation factor (tangent loss) of PZT film capacitors processed at 100/spl deg/C was 8.35%. However the dissipation factor of PZT film capacitor processed at 60/spl deg/C was only 0.35%. The dielectric constant was calculated to be 32 at 1 kHz. After annealing at 400/spl deg/C, the dielectric constant increased about 33% to 43. The dielectric constant increased to 165 after annealing at 500/spl deg/C and to 1143 after annealing at 600/spl deg/C. The PZT film capacitors produced to-date had little dependence on frequency from 20 Hz to 100 kHz. The frequency dependence increased with increasing annealing temperature from 400/spl deg/C to 600/spl deg/C. Lowering the processing temperature from 100/spl deg/C to 60/spl deg/C resulted in a tremendous decrease in the dissipation factor from 8.3% to 0.35%.


    Access

    Check access

    Check availability in my library

    Order at Subito €


    Export, share and cite



    Title :

    Low temperature processed lead zirconate titanate (PZT) film as dielectric for capacitor applications


    Contributors:


    Publication date :

    2000-01-01


    Size :

    833518 byte




    Type of media :

    Conference paper


    Type of material :

    Electronic Resource


    Language :

    English




    Lead Zirconate Titanate (PZT) Film Capacitor with a Multilayer Construction

    Tsao, B.-H. / Fries-Carr, S. / Weimer, J. et al. | British Library Conference Proceedings | 1998


    Sputtered Barium Titanate, Lead Zirconate Titanate, Barium Strontium Titanate Films for Capacitor Applications

    Tsao, Bang-Hung / Weimer, Joseph A. / Carr, Sandra Fries et al. | SAE Technical Papers | 2000


    Sputtered Barium Titanate, Lead Zirconate Titanate, Barium Strontium Titanate Films for Capacitor Applications

    Tsao, B.-H. / Carr, S. F. / Heidger, S. et al. | British Library Conference Proceedings | 2000


    Temperature Dependence of the Dielectric, Elastic and Piezoelectric Material Constants of Lead Zirconate Titanate Ceramics

    Sherrit, S. / Yang, G. / Wiederick, H. D. et al. | British Library Conference Proceedings | 1999