Thin PZT film is being developed for use in microelectronics, electromechanical and optoelectronic applications. Thin Pb(ZrTi)O/sub 3/ film capacitor devices were fabricated using RF sputtering techniques. The multiple-layer configuration of Si/SiO/sub 2//Ti/Pt was used as the substrate and bottom electrode. The top electrode was Pt. At 1 kHz, the dissipation factor (tangent loss) of PZT film capacitors processed at 100/spl deg/C was 8.35%. However the dissipation factor of PZT film capacitor processed at 60/spl deg/C was only 0.35%. The dielectric constant was calculated to be 32 at 1 kHz. After annealing at 400/spl deg/C, the dielectric constant increased about 33% to 43. The dielectric constant increased to 165 after annealing at 500/spl deg/C and to 1143 after annealing at 600/spl deg/C. The PZT film capacitors produced to-date had little dependence on frequency from 20 Hz to 100 kHz. The frequency dependence increased with increasing annealing temperature from 400/spl deg/C to 600/spl deg/C. Lowering the processing temperature from 100/spl deg/C to 60/spl deg/C resulted in a tremendous decrease in the dissipation factor from 8.3% to 0.35%.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Low temperature processed lead zirconate titanate (PZT) film as dielectric for capacitor applications


    Beteiligte:
    Bang-Hung Tsao, (Autor:in) / Heidger, S. (Autor:in) / Weimer, J.A. (Autor:in)


    Erscheinungsdatum :

    01.01.2000


    Format / Umfang :

    833518 byte




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    Sputtered Barium Titanate, Lead Zirconate Titanate, Barium Strontium Titanate Films for Capacitor Applications

    Tsao, Bang-Hung / Weimer, Joseph A. / Carr, Sandra Fries et al. | SAE Technical Papers | 2000


    Sputtered Barium Titanate, Lead Zirconate Titanate, Barium Strontium Titanate Films for Capacitor Applications

    Tsao, B.-H. / Carr, S. F. / Heidger, S. et al. | British Library Conference Proceedings | 2000


    Lead Zirconate Titanate (PZT) Film Capacitor with a Multilayer Construction

    Tsao, B.-H. / Fries-Carr, S. / Weimer, J. et al. | British Library Conference Proceedings | 1998


    Temperature Dependence of the Dielectric, Elastic and Piezoelectric Material Constants of Lead Zirconate Titanate Ceramics

    Sherrit, S. / Yang, G. / Wiederick, H. D. et al. | British Library Conference Proceedings | 1999