In the present study, the fatigue properties of a 720 ° C/1h annealed Ti‐6Al‐4V alloy have been evaluated under the following conditions: in air at room temperature (RT), in vacuum at RT and in vacuum at cryogenic temperature, using a vacuum‐cryogenic electric fatigue machine. Fracture surfaces of the fatigued specimens and the microstructures in regions adjacent to fracture surface were examined by scanning election microscopy (SEM) and transmission election microscopy (TEM). The results showed that the fatigue strength of Ti‐6Al‐4V alloy decreased in the order of the following conditions: in vacuum at cryogenic temperature, in vacuum at RT and in air at RT. The longest fatigue life of the alloy could be obtained in vacuum at cryogenic temperature, while the shortest one in air at room temperature. Crack initiation site, crack prorogation path and rapid failure zone were distinguishable on the fractured surfaces of the specimens fatigued either in air or in vacuum at room and cryogenic temperatures. Generally, the fatigue cracks initiated at the surface of the specimens and many dimples could be found in the rapid failure zone. Dislocation slip was found to be the main deformation mode under the three testing conditions.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Fatigue Properties of Ti‐6Al‐4V Alloy in Vacuum at Cryogenic Temperature


    Beteiligte:
    Dong, S. L. (Autor:in) / Lu, G. (Autor:in) / Zhang, L. Q. (Autor:in) / Yang, D. Z. (Autor:in) / He, S. Y. (Autor:in) / Han, E. H. (Autor:in) / Kleiman, Jacob I. (Herausgeber:in)

    Kongress:

    PROTECTION OF MATERIALS AND STRUCTURES FROM SPACE ENVIRONMENT: Proceedings of the 9th International Conference: Protection of Materials and Structures From Space Environment ; 2008 ; Toronto (Canada)


    Erschienen in:

    AIP Conference Proceedings ; 1087 , 1 ; 534-543


    Erscheinungsdatum :

    05.01.2009


    Format / Umfang :

    10 pages





    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch



    Fatigue Properties of Ti-6Al-4V Alloy in Vacuum at Cryogenic Temperature

    Dong, S.L. / Lu, G. / Zhang, L.Q. et al. | British Library Conference Proceedings | 2009


    Cryogenic Vacuum Pump

    Zachman, C. A. | NTRS | 1983


    CRYOGENIC-VACUUM PLANT

    GEKTIN YURIJ MIKHAJLOVICH / ZORIN SERGEJ MIKHAJLOVICH / TROFIMOV DMITRIJ OLEGOVICH et al. | Europäisches Patentamt | 2019

    Freier Zugriff

    VACUUM-CRYOGENIC STAND

    BOROVKOV DMITRIJ ALEKSANDROVICH / BURETS GALINA ALEKSANDROVNA / DENISOV ROSTISLAV NIKOLAEVICH et al. | Europäisches Patentamt | 2016

    Freier Zugriff

    High-Cycle Fatigue Properties of a Titanium Alloy at Cryogenic Temperatures (AAS 03-417)

    Ogata, T. / Matsuoka, S. / American Astronautical Society | British Library Conference Proceedings | 2004