In this paper, damage monitoring and fatigue-life prediction of cross-ply silicon carbide fiber–reinforced calcium aluminosilicate (SiC/CAS) ceramic-matrix composites (CMCs) at room temperature and elevated temperatures of 700 and 850°C in an air atmosphere have been investigated. Considering the fatigue-damage mechanisms of interface wear, interface oxidation, and fiber oxidation, the relationships among fatigue hysteresis-loop evolution, interface shear-stress degradation, broken fibers, and fatigue lifetime have been established. The evolution of damage parameters, i.e., fatigue hysteresis dissipated-energy changing rate, interface shear-stress degradation rate, broken-fiber fraction, and fatigue-life stress-cycle (S-N) curves have been analyzed. The interface shear-stress degradation rate is affected by the maximum stress level and testing environment; the fatigue hysteresis dissipated energy decreases with the applied increment cycles and experimental temperatures. The fatigue limit stresses are 50, 36, and 30% of tensile strength at room temperature and 700 and 850°C, respectively.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Damage Monitoring and Life Prediction of Cross-Ply SiC/CAS Ceramic-Matrix Composites at Room and Elevated Temperatures under Cyclic Loading


    Beteiligte:
    Longbiao, Li (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    27.10.2017




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt