The properties such as dent depth, residual compressive strength and compressive failure strain of 3 groups of T800 carbon fiber composite laminates with the same layer ratio and different thicknesses were tested. The results show that there inflection points are existed both in impact energy-dent depth curves and dent depth-residual compression strength curves. The inflection points of the 3 groups are at the depths of 0.70 mm, 0.76 mm and 0.45 mm respectively, which are less than the depth of dent (1.3 mm) corresponding to barely visible impact damage (BVID). With the same ply ratio, the greater the thickness of composite laminates, the better the impact damage resistance.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Impact Resistance of T800 Carbon Fiber Composite Materials


    Beteiligte:
    WANG Li (Autor:in) / XIONG Shu (Autor:in) / ZHAO Yan (Autor:in) / YANG Li (Autor:in)


    Erscheinungsdatum :

    2018




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Hole making characteristics of novel domestic T800 carbon fiber reinforced composite

    DONG Huimin / WANG He / MENG Fanxing et al. | DOAJ | 2023

    Freier Zugriff

    Fahrbericht: Kenworth T800

    Kenworth Truck,US | Kraftfahrwesen | 2004


    Essai: Kenworth T800 SH

    Combemale,P. / Kenworth,US | Kraftfahrwesen | 1999



    UH-1H to receive T800

    Online Contents | 1994