The low oxygen content SiC fibers were exposed in simulated aeroengine circumstance of \begin{document}${P_{{{\rm{H}}_2}{\rm{O}}}}:{P_{{{\rm{O}}_2}}}:{P_{{\rm{Ar}}}} = $\end{document}14 kPa \begin{document}$:8$\end{document} kPa \begin{document}$:78$\end{document} kPa at 1200 ℃ for 1-50 h. Performances and structure of the fibers were characterized by element analysis, XRD, SEM and tensile test. The results show that the fibers have higher oxygen content, thicker oxide layer, lower strength compared with the fibers treated in dry air. Cracks and α-SiO2 crystal are more likely to occur in silica layer. The steam in the simulated circumstance can accelerate oxidation and crack formation in silica film.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Microstructure and Mechanical Properties of Low Oxygen Content SiC Fibers in Simulated Aeroengine Circumstance


    Beteiligte:
    LI Liang (Autor:in) / MAO Xianhe (Autor:in) / JIAN Ke (Autor:in) / WANG Yifei (Autor:in) / YUAN Xiaoning (Autor:in)


    Erscheinungsdatum :

    2018




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Aeroengine and process of operating an aeroengine

    CARLOS HANNOVER GALINDO-LOPEZ | Europäisches Patentamt | 2025

    Freier Zugriff

    Cause & Circumstance

    Aarons, R. N. | British Library Online Contents | 2003


    Cause & Circumstance

    Aarons, R. N. | British Library Online Contents | 2002


    Pump and circumstance

    The Pump Guy | Online Contents | 2004