ZK60 casting magnesium alloy was subjected to friction stir processing (FSP). Defect-free joints could be obtained under a range of processing speeds (50-200 mm/min) at a constant rotation rate of 800 r/min, and microstructures and mechanical properties of the experimental materials were investigated. The results show that the coarse grains in base material are changed into fine equiaxed grains in stir zone after FSP. With the increas of processing speed, the mean grain size decreases firstly and then increases. The microhardness and tensile strength of stir zone increase compared with the base material, and the elongation increases significantly due to its fine and uniform microstructure of the specimen. The optimum properties are obtained in the specimen prepared at the processing speed of 100 mm/min, the average grain size of the specimen is 6.9 μm, and the microhardness, tensile strength and elongation are 70.1HV, 276 MPa and 31.6% respectively.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Influence of Processing Speed on Microstructure and Mechanical Properties of ZK60 Magnesium Alloy Prepared by Friction Stir Processing


    Beteiligte:
    LIN Jun (Autor:in) / ZHANG Datong (Autor:in) / ZHANG Wen (Autor:in) / QIU Cheng (Autor:in)


    Erscheinungsdatum :

    2017




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Microstructure and mechanical behavior of similar butt-joints of ZK60 and ZK60–1.5RE magnesium alloys produced by linear friction stir welding

    Silva, E.P. / Buzolin, R.H. / Alfaro Mercado, Ulises et al. | Deutsches Zentrum für Luft- und Raumfahrt (DLR) | 2021

    Freier Zugriff

    Surface Modification Effect of Magnesium Alloy by Friction Stir Processing

    Ajayan, Adarsh / Prabhu, M. K. / Ilakiya, P. et al. | SAE Technical Papers | 2024



    The Influence of Zinc and Zirconium on the Microstructure of the As-Cast Magnesium Alloy ZK60

    Ma, Y. L. / Pan, F. S. / Zuo, R. L. et al. | British Library Conference Proceedings | 2007


    Effect of Cooling Rate on the Microstructure and Mechanical Properties of ZK60 Alloy

    Lin, J. B. / Wang, Q. D. / Peng, L. M. et al. | British Library Conference Proceedings | 2007