FeNi36 (Invar-36) alloy is widely used in the fabrication of molding tools in aerospace industries but there remains a need to improve its wear and friction performance due to its relatively low hardness. The formation of a heat affected zone (HAZ) on the surface of Invar-36 cut by wire electric discharge machining (WEDM) is promising to enhance its tribological properties. This study aims to investigate the tribological performance of WEDM-treated Invar-36 via a ball-on-disk tribometer in dry-sliding conditions.
The untreated and WEDM-treated Invar-36 surfaces were reciprocated against an alumina ball at a sliding velocity of 40 mm/s, a stroke length of 10 mm and a sliding duration of 125 min under loads of 5, 10 and 20 N. The worn surfaces were characterized using a 2D profilometry and a scanning electron microscope equipped with energy-dispersive spectroscopy.
The results showed that the WEDM-treated surface had a superior friction coefficient and wear resistance in comparison to the untreated surface, due to the grown HAZ. There was found to be a 9.3%–11.4% decrease in the friction coefficient and a 47%–57% reduction in the wear volume after the WEDM treatment. Both the untreated and WEDM-treated Invar-36 surfaces found abrasion and plastic deformation as the dominant wear mechanisms.
Previous works have not focused on the tribological performance of the WEDM-treated Invar-36 extensively used for molding tools in aerospace industries. Our findings provide compelling evidence that the WEDM treatment improved the wear and friction performance of Invar-36 alloy because of the grown HAZ.
Investigation of the wear behavior of FeNi36 alloy cut by WEDM method under different loads
Aircraft Engineering and Aerospace Technology ; 96 , 1 ; 136-143
06.02.2024
8 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Surface and subsurface hardenability of AA6061-T6 aerospace alloy machined by WEDM
Emerald Group Publishing | 2025
|Emerald Group Publishing | 2024
|Investigation on Wear Behavior of Al-Si Eutectic Alloy
IEEE | 2021
|Dynamic Behavior of Rock Joint under Different Impact Loads
Online Contents | 2019
|An investigation on cutting of the cold work steel X153CrMoV12 by WEDM
Emerald Group Publishing | 2021
|