PROBLEM TO BE SOLVED: To overcome aggravation of crack growth resistance by a method of using carbon black with a large particle diameter or reducing the blended amount of oil for satisfying the requirements for a bead filler: no reduction in hardness at high temperature, low heat generation property and excellent crack growth resistance, and problems of aggravation of temperature dependency of hardness, heat generation property and crack growth resistance, due to a method of blending a thermosetting resin, although the method provides high hardness.SOLUTION: The above described problem is solved by a rubber composition for tire bead filler by blending 100 pts.mass of diene rubber containing NR of 50 to 80 pts.mass and SBR of 20 to 50 pts.mass, 60 to 90 pts.mass of carbon black having nitrogen adsorption specific area (NSA) of 25 to 85 m/g and 0.1 to 5 pts.mass of for example anthraquinone sodium sulfonate.SELECTED DRAWING: None

    【課題】ビードフィラーは高温時に硬度が低下しないこと、低発熱性であること、耐クラック成長性に優れることが求められている。そのため、大粒径のカーボンブラックを使用したり、オイルの配合量を減少する手法があるが、耐クラック成長性の悪化を招いていた。また、熱硬化性樹脂を配合する手法もあるが、高硬度は得られるものの、硬度の温度依存性、発熱性および耐クラック成長性が悪化するという問題点がある。【解決手段】NRを50〜80質量部およびSBRを20〜50質量部含むジエン系ゴム100質量部に対し、窒素吸着比表面積(N2SA)が25〜85m2/gのカーボンブラックを60〜90質量部、および例えばアントラキノンスルホン酸ナトリウムを0.1〜5質量部配合してなるタイヤビードフィラー用ゴム組成物によって上記課題を解決した。【選択図】なし


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    RUBBER COMPOSITION FOR TIRE BEAD FILLER AND PNEUMATIC TIRE USING THE SAME


    Weitere Titelangaben:

    タイヤビードフィラー用ゴム組成物およびそれを用いた空気入りタイヤ


    Beteiligte:
    SHIMIZU YUKI (Autor:in) / HIJIKATA KENSUKE (Autor:in) / ASHIURA MAKOTO (Autor:in)

    Erscheinungsdatum :

    01.09.2016


    Medientyp :

    Patent


    Format :

    Elektronische Ressource


    Sprache :

    Japanisch


    Klassifikation :

    IPC:    B60C VEHICLE TYRES , Fahrzeugreifen / C08L COMPOSITIONS OF MACROMOLECULAR COMPOUNDS , Massen auf Basis makromolekularer Verbindungen / C08K Verwendung von anorganischen oder nichtmakromolekularen organischen Stoffen als Zusatzstoffe , USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES AS COMPOUNDING INGREDIENTS



    TIRE BEAD FILLER RUBBER COMPOSITION AND PNEUMATIC TIRE USING THE SAME

    SHIMIZU YUKI / HIJIKATA KENSUKE | Europäisches Patentamt | 2016

    Freier Zugriff

    BEAD FILLER RUBBER COMPOSITION AND PNEUMATIC TIRE

    KATO MANABU / TAKAHASHI RYOTA / OKAMATSU TAKAHIRO et al. | Europäisches Patentamt | 2015

    Freier Zugriff

    BEAD FILLER RUBBER COMPOSITION AND PNEUMATIC TIRE

    KATO MANABU / TAKAHASHI RYOTA / OKAMATSU TAKAHIRO et al. | Europäisches Patentamt | 2017

    Freier Zugriff

    RUBBER COMPOSITION FOR TIRE BEAD FILLER, AND PNEUMATIC TIRE USING THE SAME

    HIJIKATA KENSUKE | Europäisches Patentamt | 2015

    Freier Zugriff

    Bead filler rubber composition and pneumatic tire

    KATO MANABU / TAKAHASHI RYOTA / OKAMATSU TAKAHIRO et al. | Europäisches Patentamt | 2017

    Freier Zugriff