We have reviewed the recent research carried out to realize all-epitaxial VCSELs at long wavelengths. Shortcomings of the InP materials system were overcome by the use of AsSb-based alloys for DBRs and multiple active regions to combat low gain materials. The inclusion of InP spreading layers was seen to greatly improve the thermal properties of the devices. Two apertures were developed for the optical and current confinement. Careful placement of these apertures is expected to improve the VCSEL performance considerably.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Current status of epitaxial 1.31-1.55 /spl mu/m VCSELs on InP


    Beteiligte:
    Reddy, M.H.M. (Autor:in) / Buell, D.A. (Autor:in) / Huntington, A.S. (Autor:in) / Koda, R. (Autor:in) / Freezell, D. (Autor:in) / Asano, T. (Autor:in) / Jim, J.K. (Autor:in) / Hall, E. (Autor:in) / Nakagawa, S. (Autor:in) / Coldren, L.A. (Autor:in)


    Erscheinungsdatum :

    01.01.2002


    Format / Umfang :

    150184 byte





    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch



    Temperature Dependence of 1.55 /spl mu/m VCSELs

    Masum, J. / Ramoo, D. / Balkan, N. et al. | IEEE | 1998


    Modulation Efficiency Enhancement of 1.55-μm Injection-Locked VCSELs

    Xiaoxue Zhao, / Change-Hasnain, C.J. / Hofmann, W. et al. | IEEE | 2006



    Integrated a hybrid CATV/GPON transport system based on 1.31/1.49/1.55 μm WDM transceiver module

    Yao-Ling Cheng, / Yi-Hsiung Lin, / Ming-Chuan Wang, et al. | IEEE | 2005