Solid state battery (SSB) is potentially favorably as energy storage for electric vehicles because of the higher energy density offered and the use of solid electrolytes with good thermal resistance that solve the safety problems induced by fluid electrolytes. However, cracks that appear during charge-discharge cycling on the SSB have not been cleared up by this recent development and ended up affecting the battery performance. This crack arises from high compressive loading cycles by the volume change of the anode and cathode during lithiation/delithiation, in which the crack propagation can affect the conductivity of solid electrolyte ions. Therefore, this study aims to determine and analyze the effect of compressive loading on the cracking of solid electrolytes toward ionic conductivity. The research was carried out by giving a compressive load of 0.15 MPa to $\mathrm{L}\mathrm{i}_{1.3}\mathrm{A}1_{0.3}\mathrm{T}\mathrm{i}_{1.7}(\mathrm{P}\mathrm{O}_{4})_{3}$ (LATP) solid electrolyte. A Cohesive Zone Element is applied to the grain boundaries of LATP solid electrolyte to simulate the cracking process. The result was analyzed and showed that ionic conductivity increases under compressive loading but was expected to decrease when the crack appears.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Finite Element Analysis of LATP Solid Electrolyte under Compressive Loading


    Beteiligte:


    Erscheinungsdatum :

    14.09.2022


    Format / Umfang :

    906097 byte




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    AIAA-2006-2003 Stochastic Finite Element Failure Analysis of Laminated Plates Under Uniaxial Compressive Loading

    Onkar, A. / Upadhyay, C. / Yadav, D. et al. | British Library Conference Proceedings | 2006


    Effect of microcracking on ionic conductivity in LATP

    Jackman, Spencer D. | Online Contents | 2012



    Finite Element Simulation of Energy Absorption Devices Under Axial Static Compressive and Impact Loading

    Webb, D. C. / Webster, J. / Kormi, K. | British Library Conference Proceedings | 2000