The research for cheap and abundant LiFeP04/C as cathode material of lithium-ion battery became a trending topic in this century. LiFePO4/C particles were commonly used due to its environmental acceptability. This research was aimed to compare methods for preparing LiFePO4/C particles using solid state and flame assisted spray pyrolysis method. The variable of studied at variation molar ratio $\mathrm{Li: Fe: P}$ of $1: 1:1\ 1.1:1:1:\ 1.2:1:1$; and $1.3: 1: 1$. The crystalline structure was characterized by X-Ray Diffraction (XRD). The morphology was characterized using SEM test. The electrochemical performance was characterized using battery analyzer. Based on data, still exhibits some impurities. The particle still in micron-sized. The highest initial discharge capacity at molar ratio $\mathrm{Li: Fe: P}$ of $1.1:1:1$ is 46.1 mAh g−1 at 1/20 C.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Fabrication and Electrochemical Performance of LiFePO4/C as Cathode Material for Lithium Ion Battery


    Beteiligte:


    Erscheinungsdatum :

    01.10.2018


    Format / Umfang :

    668877 byte




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    Synthesis and electrochemical performance of lithium-rich cathode material

    Wei, Xin / Zhang, Shichao / Liu, Guanrao et al. | British Library Online Contents | 2016



    Cathode active material for lithium secondary battery

    CHANG SUNG-KYUN / JEON HYELIM / PARK HONG KYU et al. | Europäisches Patentamt | 2015

    Freier Zugriff