The coated blade operated 16.2 hours prior to being flown in rain. Visual inspection revealed no deterioration. After 1.5 operating hours in heavy rain (to a total operating time of 17.7 hours), the coating on both blades was deteriorated to the point of failure of materiel. However, the blades remained on the helicopter until they had accumulated 55.9 operating hours. During the additional operating time the blades did not appear to deteriorate any further, but they were not operated in rain. The main-rotor blade erosion-resistant leading-edge coating is not suitable for operation in rain. Further studies be conducted through USAAVLABS to develop main-rotor-blade erosion-resistant material that is not susceptible to rain damage.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    'Product Improvement Test of UH-1 Main Rotor Blades with Erosion-Resistant Leading-Edge Coating.'


    Erscheinungsdatum :

    1968


    Format / Umfang :

    5 pages


    Medientyp :

    Report


    Format :

    Keine Angabe


    Sprache :

    Englisch




    Tungsten-based erosion-resistant leading edge protection cap for rotor blades

    MATHEW PAUL / KRISHNAMURTHY SRIRAM / SUBRAMANIAN SHANMUGA PRIYAN | Europäisches Patentamt | 2022

    Freier Zugriff


    EFFECT OF LEADING-EDGE TUDBERCLES ON ROTOR BLADES

    Colvitts, Robert R. / Perez, Ruben E. / Jansen, Peter W. | TIBKAT | 2020


    Effect of Leading-Edge Tubercles on Rotor Blades

    Colpitts, Robert R. / Perez, Ruben E. / Jansen, Peter W. | AIAA | 2020


    Application of Leading-Edge Tubercles on Rotor Blades

    Colpitts, Ryley / Perez, Ruben E. | AIAA | 2023