In new method, silsesquioxane powders blended to control ratio of carbon to silicon. Powders melted, and excess silanol groups condense with evolution of water. When melt attains suitable viscosity, extruded into fibers through die or drawn into fibers from melt at uniform rate. Fibers cured and heat treated. Enables easy fabrication of thermally stable fibers from inexpensive silsesquioxane precursors. Impregnation of fibers and preforms without solvent minimizes both shrinkage and formation of voids resulting from volatilization of trapped solvent.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Fibers And Composites Derived From Silsesquioxanes


    Beteiligte:

    Erschienen in:

    Erscheinungsdatum :

    01.12.1988



    Medientyp :

    Sonstige


    Format :

    Keine Angabe


    Sprache :

    Englisch


    Schlagwörter :


    Fluorinated Silsesquioxanes: Structure, Solubility, and Wetting (Briefing charts)

    J. Mabry / A. Guenthner / S. Iacono et al. | NTIS | 2015



    Water soluble carboxymethylcellulose fibers derived from alkalization-etherification of viscose fibers

    Gu, H. / He, J. / Huang, Y. et al. | British Library Online Contents | 2012


    High-performance composites from acetylated wood fibers

    Westin, M.S. / Simonson, R.G. | Tema Archiv | 1992


    Carbon fibers for composites

    Chand, S. | Tema Archiv | 2000