The effect of forming deformation on the corrosion performance of electroplated zinc and iron-zinc alloy coated steel was investigated. The materials were tested with (1) no deformation, (2) moderate deformation, and (3) high deformation. The formed specimens were painted, scribed, and exposed in three corrosion tests. Although significant morphological change (cracking) occurred in the deformed surfaces, the results of the corrosion testing showed that the forming had no effect on cosmetic corrosion performance. A paint adhesion evaluation revealed that forming had no effect on the paint adhesion on carbon steel, but adhesion loss increased with increased deformation on the iron-zinc coated specimens and decreased with increased deformation on zinc coated specimens. Significantly, in nearly all cases, the actual loss of adhesion for the iron-zinc-alloy coated samples was less than that on the zinc-coated or carbon-steel samples.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effect of Forming Deformation on Corrosion Test Performance of Electroplated Zinc and Iron-Zinc Alloy Coatings for Automotive Sheet


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    1986 SAE Automotive Corrosion and Prevention Conference and Exposition ; 1986



    Erscheinungsdatum :

    08.12.1986




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch





    Effect of pretreatment on performance of zinc and zinc alloy electroplated sheet in cyclic corrosion test

    Shastry,C.R. / Townsend,H.E. / Bethlehem Steel,US | Kraftfahrwesen | 1989



    Iron-zinc alloy electroplated steel for automotive body panels

    Watanabe, T. / Ohmura, M. / Honma, T. et al. | Tema Archiv | 1982


    Iron-Zinc Alloy electroplated steel for automotive body panels

    Watanabe,T. / Ohmura,M. / Honma,T. et al. | Kraftfahrwesen | 1982