Various galvanized steels, ZINCROMETAL and cold-rolled steel were painted with automotive-type paints and tested via accelerated, atmospheric and on-vehicle tests. Tests indicate that the ASTM B117 salt fog test and the Kesternich SO2 test do not yield results which are indicative of automotive, in-service corrosion performance. A modified Volvo scab corrosion test was found to offer an accelerated method to accurately predict automotive, in-service corrosion performance. Galvanized steels exhibited corrosion resistance which was far superior to ZINCROMETAL and cold-rolled steel. Thicker zinc coatings on steel were found to offer better corrosion protection to painted substrates.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    A Comparison of Corrosion Test Methods for Painted Galvanized Steel


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Nowak, E. T. (Autor:in) / Froman, G. W. (Autor:in) / Franks, L. L. (Autor:in)

    Kongress:

    SAE International Congress and Exposition ; 1982



    Erscheinungsdatum :

    01.02.1982




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    A comparison of corrosion test methods for painted galvanized steel

    Nowak,E.T. / Franks,L.L. / Froman,G.W. et al. | Kraftfahrwesen | 1982


    Effects of Galvanized Steel Defects on Painted Appearance of Exposed Panels

    Belleau, C. / Kelley, D. K. | SAE Technical Papers | 1983


    Effects of Galvanized Steel Defects on Painted Appearance of Exposed Panels

    Belleau,C. / Kelley,D.K. / Chrysler,US | Kraftfahrwesen | 1983



    The Effects of Metal Finishing on the Appearance of Painted Galvanized Steel

    Christ.C. / Armco,Res.Cent.,Middletown,US | Kraftfahrwesen | 1982