Water penetration into the paint film of car bodies causes cosmetic corrosion. The circumstances experienced by driven cars can be classified into three groups, corresponding to high, medium and low water migration, respectively. In the first group a lot of water enters into the paint/substrate interface and lifts up the film. The stability of the phosphate layer influences the adhesiveness. In the second group salt water brings about alkaline blister formation. The corrosion resistance of the substrate against alkali in cathodically polarized state determines the paint adhesion. The third group corresponds to the scab corrosion, which can be suppressed well by zinc coating layer.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Cosmetic Corrosion Mechanism of Zinc and Zinc Alloy Coated Steel Sheet for Automobiles


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE International Congress and Exposition ; 1985



    Erscheinungsdatum :

    01.02.1985




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Cosmetic corrosion mechanism of zinc and zinc alloy coated steel sheet for automobiles

    Miyoshi,Y. / Kitayama,M. / Nishimura,K. et al. | Kraftfahrwesen | 1985



    An Evaluation of Cosmetic Corrosion Performance of Zinc and Zinc Alloy Coated Steels

    Gray, B. M. / Davidson, D. D. / Stephens, M. L. et al. | SAE Technical Papers | 1986


    Corrosion Behavior of Painted Zinc and Zinc Alloy Coated Autobody Sheet Steels

    Robbins, D. J. / Smith, D. M. / Zappia, J. et al. | SAE Technical Papers | 1986


    Corrosion studies on laser welded zinc coated steel sheet

    Alehter,R. / Watkins,K.G. / Steen,W.M. et al. | Kraftfahrwesen | 1989