Open circuit storage tests of discharged Ni/H2 cells have been carried out at 20°C to understand effects of cell design parameters on capacity fading with storage and determine capacity fading mechanism. Cell design parameters studied include variations in the electrode substrate (dry powder or wet slurry sinter), active material impregnation technique (alcoholic or aqueous bath), cobalt additive concentrations (4 to 10%), KOH concentration (26 or 31%), and cell precharge (nickel or H2). Precharge had the most dominant effect of all parameters. When cells had nickel precharge, virtually no fading was observed with storage up to 188 days, while gradual fading was observed with all H2 precharged cells. Tendency of capacity fading of these cells depended on KOH concentration, impregnation technique, and cobalt concentration. Cell pressure changes with storage were consistent with build-up of electrochemically undischargeable active material with capacity fading. Overcharging at low temperature (0°C) was effective in partial recovery of capacity but low-earth-orbit cycling had a minimal effect.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effect of Cobalt Additive, KOH Concentrations, and Types of Nickel Electrodes on Storage Behavior of Nickel-Hydrogen Cells


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Lim, Hong S. (Autor:in)

    Kongress:

    27th Intersociety Energy Conversion Engineering Conference (1992) ; 1992



    Erscheinungsdatum :

    03.08.1992




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch


    Schlagwörter :





    Bending Properties of Nickel Electrodes for Nickel-Hydrogen Batteries

    Lerch, B. A. / Wilson, R. M. / Keller, D. et al. | British Library Conference Proceedings | 1996