To overcome the most serious deficiency in fiber-reinforced composite materials a three-dimensional, continuously woven material has been developed. To demonstrate the feasibility of the new weave pattern, a 0.3 in thick fabric was woven with 12-end S-glass roving and impregnated with Epon 828 epoxy resin using curing agent Z. A 24 harness semiautomatic loom was used to produce the fabric.Tension tests were conducted on the material in both the weave and transverse directions. The material exhibited maximum tensile strength of 47,000 psi and 64,000 psi in the weave and transverse directions, respectively. The elastic moduli were 2,640,000 and 3,220,000 psi, respectively.Compression tests were conducted in the weave (longitudinal), transverse, and thickness directions. The ultimate strengths in compression were 39,000, 52,000, and 71,000 psi, respectively. The elastic moduli in compression were 2,820,000, 3,410,000, and 1,240,000 psi in the three respective principal directions.The Poisson ratios were obtained for both tension and compression.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Development of a Pseudohomogeneous, Three-Dimensional, Continuously Woven Composite Material


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Reese, C. D. (Autor:in) / Forman, G. W. (Autor:in) / Faddis, T. N. (Autor:in)

    Kongress:

    National Business Aircraft Meeting and Engineering Display ; 1972



    Erscheinungsdatum :

    01.02.1972




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Three-dimensional woven composite material tension-torsion strip structure

    SUN LIDA / ZHENG JUNWEI / XIONG QINGHUI | Europäisches Patentamt | 2023

    Freier Zugriff

    Method for manufacturing rib using three-dimensional woven composite material, and rib

    YAN SHIBO / LI YIDING / ZHANG WEIJIE et al. | Europäisches Patentamt | 2025

    Freier Zugriff

    Tire with continuously woven carcass ply

    WANG YOUSHAN / SU BENLONG / WU JIAN et al. | Europäisches Patentamt | 2025

    Freier Zugriff

    Three-dimensional woven composite material carbon-based sliding plate and preparation method thereof

    WANG DA / LI LIN / WU SHENGTI et al. | Europäisches Patentamt | 2023

    Freier Zugriff