Recently, SiCr clean steel wire for springs on automotive engine valves has been developed. This report describes the characteristics of valve springs subjected to a new manufacturing process using SiCr clean steel wire. The process developed by the authors is as follows: First, form a helical spring with SiCr clean steel wire. Next, quench using the distortion preventing technic --Marquenching--. Temper at a temperature lower than the conventional temperature. Shot peen to the surface layer of the spring. And lastly, polish electrolytically to remove micro surface defects formed through shot peening. Using this new manufacturing process, a valve spring with high fatigue resistance can be produced. At the test stress of 588MPa(τm)±490MPa (τa), the number of cycles to fracture was above 100 million, while the number of cycles to fracture was 4 million using the conventional process with the SiCr clean steel which has the best fatigue resistance for commercial use.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Valve Spring with High Fatigue Resistance for Automotive Engine


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE International Congress and Exposition ; 1988



    Erscheinungsdatum :

    01.02.1988




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Valoe spring with high fatigue resistance for automotive engine

    Shibata,T. / Yamamoto,S. / Hashimoto,Y. et al. | Kraftfahrwesen | 1988





    High Strength Light-Weight Valve Spring for Automotive Engine to Enhance Fuel Efficiency

    Ban, Hyung Oh / Lee, Jung-Suk / Ko, Young Sang | SAE Technical Papers | 2012