The adhesive bonding performance of automotive-type galvanized sheet steels was investigated using several epoxy adhesive/surface lubricant combinations. Environmental durability was assessed through exposure to cyclic accelerated corrosion tests.Results revealed that for both ambient and environmentally exposed samples, both strength and failure mode performance were strongly dependent upon the specific adherend/adhesive combination. Environmentally induced strength degradation in joints of uncoated and zinc coated steels was attributed to corrosion at the adherend/ adhesive interface. The reason for strength losses in zinc-iron coated steel joints was apparently different, and is not clear at this time.Implications are that for optimum environmental durability, adherends, adhesives and lubricants should be selected using a systems approach.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Environmental Durability of Epoxy Adhesive/Galvanized Steel Tensile Shear Joints


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE International Congress and Exposition ; 1988



    Erscheinungsdatum :

    01.02.1988




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Environmental durability of epoxy adhesive/galvanized steel tensile shear joints

    Natale,T.V. / National Steel,Product Application Center,US | Kraftfahrwesen | 1988


    Surface Modification for Improved Adhesive Bond Durability on Galvanized Steel

    Coduti, P. L. / Paratore, L. J. / SAE | British Library Conference Proceedings | 1997


    Surface modification for improved adhesive bond durability on galvanized steel

    Coduti,P.L. / Paratore,L.J. / Inland Steel Research Labs.,US | Kraftfahrwesen | 1997


    Surface Modification for Improved Adhesive Bond Durability on Galvanized Steel

    Paratore, Leo J. / Coduti, Phillip L. | SAE Technical Papers | 1997