The Corrosion Task Force of the Automotive/Steel Partnership (A/SP) and the Society of Automotive Engineers' Automotive Corrosion and Prevention (SAE/ACAP) committee are working cooperatively on the development of an improved laboratory test for perforation corrosion. This paper gives the results of testing a set of standard SAE perforation corrosion test specimens for up to 160 cycles in the environment of J 2334, the new SAE cyclic test for cosmetic corrosion. SAE J 2334 was found to provide a clear distinction among the test materials. In general, the results indicate that the perforation corrosion resistance of coated products is much greater than that of cold rolled steel, and that it also increases with coating mass, as well as with application of a barrier organic coating. Magnetite (Fe3O4) was the predominant iron corrosion product found in the crevices of the perforation corrosion test specimens. Smaller amounts of goethite (α-FeOOH) were also found. Zincite (ZnO) was the only zinc corrosion product found in the crevices of the zinc and zinc-alloy test specimens. These results will be compared to those of on-vehicle tests of identical specimens currently being conducted at St. John's, Newfoundland; Montreal, Quebec; and Detroit, Michigan.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Laboratory Perforation Corrosion Tests of Autobody Steel Sheet


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE International Congress and Exposition ; 1997



    Erscheinungsdatum :

    24.02.1997




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Laboratory Perforation Corrosion Tests of Autobody Steel Sheet

    Townsend, H. E. / SAE | British Library Conference Proceedings | 1997


    Laboratory perforation corrosion tests of autobody steel sheet

    Townsend,H.E. / Bethlehem Steel,US | Kraftfahrwesen | 1997


    Perforation Corrosion Performance of Autobody Steel Sheet in On-Vehicle and Accelerated Tests

    Tiburcio, Butch / Meade, Cindy / Davidson, Dennis et al. | SAE Technical Papers | 2003


    Perforation corrosion performance of autobody steel sheet in on-vehicle and accelerated tests

    Davidson,D. / Thompson,L. / Lutze,F. et al. | Kraftfahrwesen | 2003


    2003-01-1238 Perforation Corrosion Performance of Autobody Steel Sheet in On-Vehicle and Accelerated Tests

    Davidson, D. / Thompson, L. / Lutze, F. et al. | British Library Conference Proceedings | 2003