The objective of this project is to quantify structural degradation due to corrosion through a fracture mechanics based approach. The metric parameters employed are Equivalent Initial Flaw Size and general material loss. Another objective is to correlate a measurable property to the amount of structural durability damage from corrosion, ideally through current NDE technology, with eddy-current as the primary choice. The approach is comprised by the following areas: corroding aluminum alloys, evaluation of the corrosion through techniques such as surface roughness and eddy current, cyclic testing, calculation of corrosion metric, and, correlation between corrosion metric and physically measurable properties.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Fracture Mechanics Based Approach for Quantifying Corrosion Damage


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    General, Corporate & Regional Aviation Meeting & Exposition ; 1999



    Erscheinungsdatum :

    20.04.1999




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Fracture Mechanics Based Approach for Quantifying Corrosion Damage

    Scheuring, J. N. / Grandt, A. F. / SAE | British Library Conference Proceedings | 1999


    Rock and Soil Damage-Fracture Space Mechanics: Damage-Fracture Space

    Dang, F. | British Library Conference Proceedings | 2007


    Rock and Soil Damage-Fracture Space Mechanics: the Divisional Damage-Fracture Theory

    Dang, F. / Chen, H. / Ding, W. et al. | British Library Conference Proceedings | 2007



    Cumulative damage fracture mechanics at elevated temperatures

    Sims, D.L. / Annis, C.G. jun. / Wallace, R.M. | Tema Archiv | 1977