AA7075 is susceptible to localized corrosion like exfoliation corrosion (EXCO), intergranular corrosion (IGC), and stress corrosion cracking (SCC). Its susceptibility is strongly affected by heat treatments. In this study, the effects of two heat treatments applied to AA7075 alloy at a different time and temperature on EXCO, IGC, and SCC were investigated. Furthermore, a joining corrosion evaluation using self-piercing riveting (SPR) was conducted. It was concluded that, when compared to the traditional T6 aging process, the samples subjected to a novel advanced aging process with a significantly reduced aging time were comparable with respect to the resistance to EXCO, IGC, SCC, and SPR joining corrosion.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effects of Heat Treatment on Exfoliation Corrosion, Intergranular Corrosion, Stress Corrosion Cracking, and Joining Corrosion of AA7075 with Advanced Aging and T6


    Weitere Titelangaben:

    Sae Int. J. Mater. Manf
    Sae International Journal of Materials and Manufacturing


    Beteiligte:
    Wu, Cedric (Autor:in) / Saltzmann, Daniel (Autor:in) / Kaunitz, Leon (Autor:in) / Chen, Zhong (Autor:in)


    Erscheinungsdatum :

    21.07.2020


    Format / Umfang :

    11 pages




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Exfoliation Corrosion and Stress Corrosion Cracking Behaviour of Al-Li Alloys

    Braun, R. / Advisory Group for Aerospace Research and Development; Structures and Materials Panel | British Library Conference Proceedings | 1995


    Stress-Corrosion Cracking Evaluation of Hot-Stamped AA7075-T6 B-Pillars

    Wright, David / Henshaw, John / Harrison, Nia R. et al. | SAE | 2017


    Stress-Corrosion Cracking Evaluation of Hot-Stamped AA7075-T6 B-Pillars

    Wright, David / Henshaw, John / Harrison, Nia R. et al. | British Library Conference Proceedings | 2017


    Controlling stress-corrosion cracking

    Franklin, D. B. / Herring, H. W. / Humphries, T. S. et al. | NTRS | 1977


    Microscopy study of intergranular stress corrosion cracking of X-52 line pipe steel

    Elboujdaini, M. / Li, J. / Fang, B. et al. | Tema Archiv | 2006