Powertrain applications of alloy AJ62 arose from its comparative resistance to high temperature deformation among magnesium alloys. In this research, AJ62 permanent-mould cast in different section thicknesses was subjected to immersion corrosion in commercially-available engine coolant. The objective was to determine corrosion behaviour variation among casting thicknesses. Corrosion product accumulation suggests passive film formation, and unlike in other media, the film exhibits certain stability. Extreme thicknesses were used to generate polarization curves for their respective microstructures in engine coolant. Variation with casting section thickness was observed in the curves. These preliminary results indicate coarsened microstructures reduce corrosion resistance of the permanent mold cast AJ62 alloy.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Microstructure Influence on the Corrosion of Permanent Mould Cast Magnesium Alloy AJ62 in Engine Coolant


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:
    Hu, Henry (Autor:in) / Burns, Jonathan Robert (Autor:in) / Han, Lihong (Autor:in) / Nie, Xueyuan (Autor:in)

    Kongress:

    SAE 2010 World Congress & Exhibition ; 2010



    Erscheinungsdatum :

    12.04.2010




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch





    Effects of Ni, Cu, Si and Co on the Corrosion Properties of Permanent Mould Cast Medallions and Die Cast Plates of Magnesium Alloy AZ91

    Bakke, P. / Sannes, S. / Albright, D. et al. | British Library Conference Proceedings | 1999



    Corrosion fatigue of cast aluminum alloys in engine coolant

    Ladwein, Thomas L. / Ripberger, Ralf | Tema Archiv | 2007


    Mechanical Property Evaluation of Permanent-Mould Cast AM-SC1TM Mg-Alloy

    Kunst, M. / Fischersworring-Bunk, A. / Gibson, M.A. et al. | British Library Conference Proceedings | 2008