A thin dense chromium coating has been developed that extends bearing life, particularly in problem environments. The coating possesses exceptional adhesion to the base metal, which allows it to withstand the extremely high unit loads present in bearing raceways.In conventional bearings life typically ends due to wear or an ultimate material failure in the raceway or rolling element. The actual cause of the failure can stem from many factors. Corrosion, contamination, loss of or poor lubrication, and mechanical damage, all accelerate failure. The coating reduces the detrimental impact of these factors, thus extending bearing life.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Extending Bearing Life in Off-Highway Equipment


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    1984 SAE International Off-Highway and Powerplant Congress and Exposition ; 1984



    Erscheinungsdatum :

    01.09.1984




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Extending Bearing Life in Off-Highway Equipment

    Waskiewicz,W.P. / Textron,Fafnir Bearing Div.,US | Kraftfahrwesen | 1984



    Bearing Design for off-highway equipment

    Society of Automotive Engineers | TIBKAT | 1982


    Extending Bearing Life Under Heavy Haulage Condition

    Rowcliffe, M. / International Heavy Haul Association / Railway Technical Society of Australia | British Library Conference Proceedings | 2001