The use of tailored-blanks is increasing in the automotive industry as manufacturers attempt to join dissimilar steel grades and thicknesses for parts consolidation and vehicle weight savings. Two methods, laser welding in a square-butt joint and resistance mash-seam welding of overlapped edges, have been used for select applications. Several automotive grade coated sheet steels were laser and mash-seam welded and evaluated for weld integrity, formability, and corrosion resistance. Salt spray and cyclic laboratory tests, and on-vehicle exposures were used for corrosion resistance evaluations. Regarding the corrosion performance of welded parts, it was observed that the weld area provided the weakest corrosion resistance on any given panel. The corrosion performance was, in part, a function of the width of the weld fusion zone. Additionally, the paint adhesion and the corrosion resistance of the welds were greatly influenced by surface oxidation and impurities within the fusion zone, variability of the joined coated substrate structure traversing the weld, and the extent of damaged coating in the heat affected zone as these items affected the subsequent phosphatability of the weld area.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Corrosion Performance of Laser and Mash-Seam Welded Automotive Sheet Steels


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    SAE Automotive Corrosion and Prevention Conference and Exposition ; 1993



    Erscheinungsdatum :

    01.10.1993




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Corrosion performance of laser and mash-seam welded automotive sheet steels

    Roudabush,L.A. / US Steel Group,US | Kraftfahrwesen | 1993


    Performance of Mash Seam Welds in Tailor Welded Blanks

    Uchihara, M. / Takahashi, M. / Kurita, M. et al. | British Library Online Contents | 1998


    Formability of mash seam welded blanks:effects of welding set-up conditions

    Bhatt,K.K. / Eisenmenger,M. / Shi,M.F. et al. | Kraftfahrwesen | 1995


    Formability of Mash Seam Welded Blanks: Effects of Welding Set-Up Conditions

    Bhatt, K. K. / Eisenmenger, M. / Shi, M. F. | SAE Technical Papers | 1995


    Tailored Blank Welding By The Resistance Mash Seam Process

    Geiermann, T. / Davenport, F. | British Library Conference Proceedings | 1995