The residual stresses produced by static and progressive induction hardening processes were investigated using different diameter bars and different heating conditions. The x-ray diffraction method of stress measurement was used. Compressive stresses were observed at and slightly below the surface in the hardened zone, while lower compressive stresses or tensile stresses were seen at the ends of this zone. These stresses depended on the shapes and sizes of the heated zone and the cooling patterns. Shot peening was seen to convert the tensile stress to a compressive value.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Residual Stress in the Induction Hardened Surface of Steel, 1969


    Weitere Titelangaben:

    Sae Technical Papers


    Beteiligte:

    Kongress:

    Mid-Year Meeting ; 1969



    Erscheinungsdatum :

    01.02.1969




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Residual Stress in the Induction Hardened Surface of Steel, 1971

    Ishii, Kentaro / Iwamoto, Mitugi / Shiraiwa, Toshio et al. | SAE Technical Papers | 1971



    Residual Stress Measurements in Case-Hardened Steels

    Horisawa, Hiroshi / Motoyama, Moritaro | SAE Technical Papers | 1971