A metallurgical examination was performed on a failed blade lag shock absorber from the aft red rotor blade of an Army cargo helicopter. The U.S. Army Research Laboratory (ARL) and the primary contractor performed a visual examination of the failed part, fluorescent penetrate inspection, fractographic evaluation, metallography, hardness testing, conductivity testing and chemical analysis. It was concluded that the part failed in fatigue from an area exhibiting intergranular attack. The corrosive attack was most likely caused by the processing fluids used during the rework process, as it was later determined that an unapproved aqueous alkaline immersion cleaner was being used. Failure to meet the required yield strength may have been an indication that the parts were not properly aged. An improper aging treatment could have facilitated the intergranular attack.
Metallurgical Examination of a Failed Blade Lag Shock Absorber from an Army Cargo Helicopter
Sae Technical Papers
Advances In Aviation Safety Conference & Exposition ; 2000
11.04.2000
Aufsatz (Konferenz)
Englisch
Metallurgical Examination of a Failed Blade Lag Shock Absorber from an Army Cargo Helicopter
British Library Conference Proceedings | 2000
|Survey of the Army Cargo Helicopter Pilot Course
NTIS | 1957
|Helicopter blade vibration absorber fatigue test device
Europäisches Patentamt | 2023
|