The damage of K9 glass under 248nm ultraviolet pulsed laser irradiation was studied. The laser pulse energy was kept within the range of 60mJ to 160mJ, and the repetition rate was adjusted within the range of 1Hz to 40Hz. The damage morphologies of single-pulse and multi-pulse laser irradiation were characterized by optical microscope, and the damage mechanism was discussed. The experimental results indicated that the damage of K9 glass irradiated by 248nm ultraviolet laser mainly followed the thermal-mechanical coupling mechanism and the damage threshold of K9 glass was 2.8J/cm2. The intensity of damage area increased gradually with the increase of the laser pulse number. It was shown that accumulation effect of laser induced damage to K9 glass was obvious.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Study on damage of K9 glass under 248nm ultraviolet pulsed laser irradiation


    Beteiligte:
    Wang, Xi (Autor:in) / Fang, Xiaodong (Autor:in)

    Kongress:

    Selected Papers from Conferences of the Photoelectronic Technology Committee of the Chinese Society of Astronautics 2014, Part II ; 2014 ; China,China


    Erschienen in:

    Erscheinungsdatum :

    13.04.2015





    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch





    157nm-248nm Multiwavelength Excitation Processing for Application in Optoelectronic Manufacturing

    Obata, K. / Sugioka, K. / Akane, T. et al. | British Library Conference Proceedings | 2001


    Teflon sputtering under pulsed CO/sub 2/-laser irradiation

    Fedenev, A.V. / Alekseev, S.B. / Orlovskii, V.M. et al. | IEEE | 2003