Abstract The environmental impact of using petroleum products has become a serious issue nowadays. This paper is about the possibility of producing ultra-lightweight concrete by using bio-polymer aggregate as a replacement for petroleum polymer. Expanded poly-lactic acid (EPLA) and Expanded Vermiculite (EV) are used as aggregate in producing biopolymer concrete. In total, five concrete mixtures are designed with varying EPLA and EV contents. The cement content and effective water-cement ratio are kept constant. The EV aggregate was replaced with EPLA aggregate in the ratio of 20%, 40%, 60% and 80%. Three types of curing conditions were used. The mechanical properties, thermal properties, electrical properties of biopolymer concrete were assessed and analysed. The microstructure of concrete was assessed after 28-days and one year. It was found that the properties of EPLA concrete are mainly influenced by the volume of EPLA and curing conditions. The chemical reactivity of EPLA significantly changes the hydration products of concrete and causes concrete carbonation as well as the conversion of hydration products to more calcium carbonate. However, at the long-term investigation (after a year) the more C-S-H gel was found. Furthermore, EPLA aggregates shrunk and lost their strength in the alkaline environment of cement.
Ultra-lightweight Concrete Containing Expanded Poly-lactic Acid as Lightweight Aggregate
KSCE Journal of Civil Engineering ; 22 , 10 ; 4083-4094
23.07.2018
12 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Ultra-lightweight Concrete Containing Expanded Poly-lactic Acid as Lightweight Aggregate
Online Contents | 2018
|Structural Lightweight Concrete Containing Recycled Lightweight Concrete Aggregate
Online Contents | 2018
|Structural Lightweight Concrete Containing Recycled Lightweight Concrete Aggregate
Springer Verlag | 2017
|PLAPoly Lactic Acid Eco-friendly lightweight PLA Poly Lactic Acid unmanned aerial vehicle
Europäisches Patentamt | 2024
|The lightweight aggregate concrete bridge at redesdale
TIBKAT | 1983
|