The corrosion of three-coated electrogalvanized steel (EG) and cold-rolled steel sheet (CR) has been investigated to evaluate their potential for outer side panels of automobile. It was found that, in the salt test, the average width of blisters on the three-coated EG was larger than that on CR. However, in the cyclic corrosion test, which is considered to simulate the actual dry and wet corrosion environment more accurately, CR showed less corrosion resistance, while EG showed high corrosion resistance, that is, no blisters or rust were found on the three-coated EG.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Effect of zinc coating on cosmetic corrosion in automotive body panel


    Weitere Titelangaben:

    Einfluss der Verzinkung auf die kosmetische Corrosion bei Karosserieblechen


    Beteiligte:
    Honjo, T. (Autor:in) / Kurokawa, S. (Autor:in) / Kimura, H. (Autor:in) / Irie, T. (Autor:in)


    Erscheinungsdatum :

    1983


    Format / Umfang :

    12 Seiten, 12 Bilder, 6 Tabellen, 7 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Effect of Zinc Coating on Cosmetic Corrosion in Automotive Body Panel

    Honjo,T. / Kurokawa,S. / Kimura,H. et al. | Kraftfahrwesen | 1983


    The Effect of Coating Iron Content on the Cosmetic Corrosion Performance of Electrodeposited Zinc-Iron Alloy Coated Sheet

    Roudabush, L. A. / NACE; Task Group T-14A on Automotive Corrosion | British Library Conference Proceedings | 1992


    Effect of panel surface roughness on automotive coating appearance

    Akutsu,E. / Kurabayashi,O. / Shibano,M. et al. | Kraftfahrwesen | 1985


    Automotive body panel feature classification

    Harmanto,D. / Blount,G.N. / Jones,R.M. et al. | Kraftfahrwesen | 1998


    Automotive Body Panel Surface Classification

    Wagimin, D. H. / Blount, G. N. / Jones, R. M. et al. | British Library Conference Proceedings | 1998