An investigation was carried out to determine the effect of the microstructure of nodular cast iron (NCI) on its cavitation corrosion behavior in natural seawater. The cavitation tests were conducted using a cavitation-induced facility at a frequency of 20 kHz on detached specimens. Morphological examinations on cavitated specimens indicated that the surface of NCI became very rough with large size cavity pits. Examination by optical microscopy of cross-sectioned specimens revealed the presence of microcracks in the bottom of cavity pits. Localized material removal on the NCI surface was due to ductile tearing and brittle modes of failure.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Cavitation corrosion of nodular cast iron (NCI) in seawater - Microstructural effects


    Weitere Titelangaben:

    Kavitationskorrosion von Gußeisen mit Kugelgraphit in Seewasser - Mikrogefügeeinfluß


    Beteiligte:
    Al-Hashem, A. (Autor:in) / Abdullah, A. (Autor:in) / Riad, W. (Autor:in)

    Erschienen in:

    Materials Characterization ; 47 , 5 ; 383-388


    Erscheinungsdatum :

    2001


    Format / Umfang :

    6 Seiten, 11 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    NODULAR CAST IRON

    Vennerholm, Gosta / Bogart, H.N. / Melmoth, R.B. | SAE Technical Papers | 1950


    Nodular cast iron steering part

    YU SEN | Europäisches Patentamt | 2015

    Freier Zugriff

    Nodular Cast Iron Monobloc Pistons

    Kunberger,K. / Karl Schmidt,Neckarsulm | Kraftfahrwesen | 1980


    Designing cast nodular iron crankshafts

    Hartwell,E. / Laystall Engineering and Qualcast,GB | Kraftfahrwesen | 1986


    Directional Solidification of Nodular Cast Iron

    Curreri, P. A. / Stefanescu, D. M. / Hendrix, J. C. | NTRS | 1987