Seven homologous imidazoline inhibitors, the derivatives of cyclopentylic and cyclohexylonaphthenic acids, have been synthesised. The effectiveness of these inhibitors for St3S steel and 1H18N9T austenitic stainless steel was tested using the impedance method in solutions of 2 wt-%NaCl, 2 wt-%NH4Cl, and 2 wt-%HCl in the presence of a hydrocarbon phase (gasoline). The solution was saturated with hydrogen sulphide. It was found that the inhibitors and their mixtures displayed high inhibition efficiencies, reaching 93% for carbon steel and 94% for the austenitic steel. Inhibitors with the shortest hydrocarbon side chains on the imidazoline ring were found to offer the lowest level of protection, the inhibition efficiency increasing with the length of the side chain. The capacitance measured on the surface decreased linearly as the coverage of the steel surface by inhibitor increased. The results of impedance measurements with commercial inhibitors have confirmed the conclusions form the tests on the pure chemical species.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Impedance study of imidazoline inhibitors against hydrogen sulphide corrosion of steel


    Weitere Titelangaben:

    Impedanzmessung von Imidazolin-Inhibitoren gegen die Schwefelwasserstoffkorrosion von Stahl


    Beteiligte:

    Erschienen in:

    British Corrosion Journal ; 37 , 2 ; 141-146


    Erscheinungsdatum :

    2002


    Format / Umfang :

    6 Seiten, 6 Bilder, 7 Tabellen, 24 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    CO2 corrosion inhibition of X-70 pipeline steel by carboxyamido imidazoline

    Ortega-Sotelo, D.M. / Gonzalez-Rodriguez, J.G. / Neri-Flores, M.A. et al. | Tema Archiv | 2011