The use of powder metallurgy (P/M) materials and processes provides several advantages over the use of wrought materials and conventional manufacturing processes for producing cost effective, high volume, high strength automotive components. Most structural parts, however, will experience some kind of periodic loads during their life cycle that exceed normal service loads. These overloads have been shown by researchers to significantly affect fatigue life. In the present study a fatigue evaluation was conducted on laboratory specimens of powder metallurgy steel with a density of 7.2 g/cm3 to determine the effect of periodic compressive overloads on fatigue life. The base material used for the pressed and sintered samples was Distaloy HP-1 powder with a composition of 0.7 Cu-4.0 Ni-1.4 Mo-2.0 Cu %wt. Monotonic tensile values and microstructure of the test samples are characterized. Strain based constant amplitude, R = -1 , fatigue tests were used to obtain baseline strain-life properties and determine the cyclic stress-strain behavior of the material. A series of periodic compressive overload tests were compared to the baseline R = -1 strain-life curve. In addition, test results are compared to powder-forged 2% Cu steel. Results showed that a variable amplitude fatigue test history, consisting of a cmpressive overload cycle followed by smaller cycles, caused a fatigue strength reduction of 55% at 1.0x106 cycles when compared to the constant amplitude fatigue results.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    The effect of periodic overloads on the fatigue behavior of powder metallurgy steel


    Beteiligte:


    Erscheinungsdatum :

    2003


    Format / Umfang :

    9 Seiten, 8 Bilder, 2 Tabellen, 13 Quellen



    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Fatigue Behavior of Neat and Short Glass Fiber Reinforced Polymers under Two-Step Loadings and Periodic Overloads

    Eftekhari, Mohammadreza / Fatemi, Ali / Khosrovaneh, Abolhassan | British Library Conference Proceedings | 2016


    Fatigue Behavior of Neat and Short Glass Fiber Reinforced Polymers under Two-Step Loadings and Periodic Overloads

    Khosrovaneh, Abolhassan / Fatemi, Ali / Eftekhari, Mohammadreza | SAE Technical Papers | 2016



    Effect of overloads on fatigue crack growth regularity within steel-molded pieces of freight cars

    Moskvitin, G. V. / Lebedinskii, S. G. | British Library Online Contents | 2013


    Effects of Compressive Overloads on Fatigue Crack Growth

    T. M. HSU ANDL. W. LASSITER | AIAA | 1975