The DP600 steels have presented new challenges to the conventional practice of resistance spot welding. In developing process requirements to spot weld stacks of two identical DP600 steel sheets, a statistical method was applied in order to establish empirical relationships between the type of weld fracture during quality control (i.e., interfacial vs. button pullout), the weld current, the weld time, and the sheet thickness independent of chemical composition and galvanized coating. The selected methodology was so successful that maps to select process parameters were developed for spot welding 0.9- to 2.2-mm-thick DP600 steels. This study also confirmed that weld diameter was a primary factor influencing type of weld fracture. A new relationship between minimum weld diameter to prevent interfacial fracture during quality control and sheet thickness was also determined, and compared with several resistance spot weld standards.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Development of requirements for resistance spot welding dual-phase (DP600) steels. Part 2: Statistical analyses and process maps


    Beteiligte:
    Marya, M. (Autor:in) / Gayden, X.Q. (Autor:in)

    Erschienen in:

    Welding Journal, New York ; 84 , 12 ; 197s-204s


    Erscheinungsdatum :

    2005


    Format / Umfang :

    8 Seiten, 16 Bilder, 15 Quellen



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch





    On Characteristics of DP600 Resistance Spot Welds

    Thompson, Andrew K. / Jiang, Chonghua / Pakalnins, Eric et al. | SAE Technical Papers | 2003


    On characteristics of dp600 resistance spot welds

    Milititsky,M. / Pakalnins,E. / Jiang,C. et al. | Kraftfahrwesen | 2003


    2003-01-0520 On Characteristics of DP600 Resistance Spot Welds

    Milititsky, M. / Pakalnins, E. / Jiang, C. et al. | British Library Conference Proceedings | 2003


    Resistance Spot Welding (RSW) Process Optimization for Coated and Uncoated Dual Phase 780 Steels

    Wexler, Arnon / Maatz, Donald F. / Koganti, Ramakrishna et al. | SAE Technical Papers | 2008