Adhesive bonded joints have been investigated due to their growing importance in aeronautic, aerospace, and automotive industries. This article examines the durability of adhesive bonded 2024 T3 aluminium alloy joints by comparing the stiffnesses of the two interfaces before and after exposure to a hot atmosphere (70 degrees C) for several cycles each of 67 hours. The stiffnesses values are calculated by ultrasonic measurements via an equivalent rheological model where the two aluminium/adhesive interfaces are replaced by an uniform distribution of longitudinal and transversal springs without inertia. Before any ageing, and for all studied specimens, the adhesion was increased by pretreating the metal by phosphoric acid pickling prior to bonding. During the first cycle of ageing, the complete crosslinking of the adhesive is observed. This phenomenon involves an increase of Young modulus of the adhesive. For the three following cycles of ageing, a small degradation of the structural joint is observed, and several hypothesis are examined. These different observations are obtained by a theoretical and experimental study of guided Lamb modes of the structure.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Ultrasonic measurements of pretreated aluminium joints durability during hot cycles


    Weitere Titelangaben:

    Ultraschallmessungen der Haltbarkeit von vorbehandelten Aluminiumverbindungen bei Temperaturwechselbeanspruchungen


    Beteiligte:

    Erschienen in:

    Erscheinungsdatum :

    2009


    Format / Umfang :

    14 Seiten, 7 Bilder, 4 Tabellen, 35 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Durability of Ni anodes during reoxidation cycles

    Ettler, M. | Online Contents | 2010


    Corrosion of pretreated aluminium after cathodic electrodeposition of paint

    Beck, F. / Blecher, A. / Krüger, U.A. et al. | Tema Archiv | 1995


    GI tripode joints - calculation of durability

    Ley, J.-P. / IMechE; Automobile Division / IEE | British Library Conference Proceedings | 1996


    GI tripode joints - calculation of durability

    Ley,J.P. / GKN Glaenzer Spicer,FR | Kraftfahrwesen | 1996


    Electrocatalyst durability under simulated automotive drive cycles

    Uchimura, Masanobu / Sugawara, Seiho / Suzuki, Yosuke et al. | Tema Archiv | 2008