Three different copper alloys have been studied, a Cu-ETP, a copper-silver alloy, Cu-AgO,l, and a copper-magnesium alloy, Cu-MgO,5. The materials were received in form of contact wire for railway applications with sections that ranged from 107 to 150 mm(exp2). The chemical compositions of the samples were determined by optical emission spectrophotometry and the oxyigen contents of the three samples were calculated by methods of quantitative metallography. In order to obtain a more detailed characterization of these materials, their mechanical and electrical properties were measured (tensile strength, the elongation at break and electrical conductivity). Microhardness, MH, was determined at room temperature (211 deg C) by using a Shimadzu model M microhardness tester that was equiped with a Vickers indenter. A contact time of 15 s and a 500 N load were employed. The reported values were obtained by averaging the results of six indentations and the intervals of confidence (95 % confidence level) for these measures were lower than 2 % of the mean values. The wear experiments were carried out by using a Microtest pin-on-disc high temperature tribometer that was provided with a 4 mm diameter hardened steel ball 52100. The hardness value for the ball was 60 HRC. The test were done over transversal sections of the wires that were previously polished for obtaining an average roughness (Ra) lower than 0.25 micrometer. A normal contact load of 5 N was applied on the surface of the specimens. A sliding speed of 0,075 m/s was selected for all the experiments and the test duration was 50 min and, consequently, the wear path that corresponds to these settings is 225 m. The samples were tested at different temperatures ranging from 20 to 350 deg C. The magnitude of the wear was determined by the difference between the weight of the samples before and after the test. The reported values are the average of several measurements and standard deviations range from 20 to 30 % of the average.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Study of the abrasive wear behaviour of electrified railway wires


    Weitere Titelangaben:

    Studie über das Abrasivverschleißverhalten von elektrischen Eisenbahnfahrdrahts


    Beteiligte:
    Garcia, A. (Autor:in) / Lorenzo, V. (Autor:in) / Varela, A. (Autor:in) / Camba, C. (Autor:in) / Blazquez, V. (Autor:in)


    Erscheinungsdatum :

    2009


    Format / Umfang :

    5 Seiten, 3 Bilder, 2 Tabellen, 7 Quellen



    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Electrified railway suspension system

    WANG XINGQUAN / JIANG XIANGUO / JIN SHOUJIE et al. | Europäisches Patentamt | 2023

    Freier Zugriff

    Abrasive wear of railway track by solid contaminants

    Grieve, D.G. / Dwyer-Joyce, R.S. / Beynon, J.H. | Tema Archiv | 2001


    Abrasive wear of railway track by solid contaminants

    Grieve, D.G. | Online Contents | 2001


    Abrasive wear of railway track by solid contaminants

    Grieve, D. G. / Dwyer-Joyce, R. S. / Beynon, J. H. | British Library Online Contents | 2001


    Abrasive wear of railway track by solid contaminants

    Grieve, D. G. / Dwyer-Joyce, R. S. / Beynon, J. H. | SAGE Publications | 2001