In this work, the stress ratio effect on FCP of longitudinal welded joint regions of an API X-70 steel under constant amplitude loading and variable amplitude loading under a single cycle peak tensile application was investigated. The results obtained lead to the following conclusions. The longitudinal welded joint regions subjected to R 0.5 initially presented the highest FCP rates in the constant amplitude tests. At higher A/C values all welded joint regions present similar behaviour indicating that the FCP rates get more independent from the i-values. The similarity between crack growth rates at high A/C in each region may indicate a dominant crack growth mechanism or a decreasing of crack closure phenomena. The discrepancy between values from Paris constants may indicate an influence of the microstructure on FCP of the welded joints investigated. Single peak tensile application on variable amplitude tests promoted delays on FCP rates in all welded joint regions for both values, as expected. However, the propagation delay was not observed at elevated values. The higher amount of secondary microcracks at elevated AK values promoted by application can explain this behaviour.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Fatigue crack propagation in API 5L X-70 pipeline steel longitudinal welded joints under constant and variable amplitudes


    Beteiligte:


    Erscheinungsdatum :

    2011


    Format / Umfang :

    8 Seiten, 10 Bilder, 5 Tabellen, 30 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch





    Improving fatigue performance of welded joints of X65 pipeline steel by UIT

    Liu, Jinming / Chen, Tong / Zhang, Yufeng | Tema Archiv | 2005



    Fatigue-crack propagation under variable-aplitude loading

    Schijve, J. / Broeck, D. / Rijk, P. | TIBKAT | 1961


    Fatigue Life Prediction for Arc Welded Joints under Variable Amplitude Loading

    Yoshida, Y. / Seto, A. / Ushioda, K. et al. | British Library Online Contents | 2013