Linear sweep voltammetry, electrochemical impedance spectroscopy, scanning electron microscopy, and x-ray diffraction techniques were used to characterize the corrosion process of API X52 steel in a solution simulating clay soil. Likewise, the formation of the corrosion products that modify their chemical composition and roughness as a function of the immersion time as a result of the presence of molecular oxygen, chloride, and sulfate ions was analyzed. It was observed that these species induce the nucleation and growth of the pitting damage. This time-dependent phenomenon enhances the steel oxidation and is responsible for the formation of magnetite, maghemite, lepidocrocite, and goethite on the steel surface. These iron compounds are important because of their semiconductor properties that may affect the polarizability of the structure of buried pipelines in different ways.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Corrosion process of API X52 carbon steel immersed in an aqueous solution simulating a clay soil


    Weitere Titelangaben:

    Korrosionsprozess des Kohlenstoffstahles API X52 in einer den tonhaltigen Erdboden simulierenden wässrigen Lösung


    Beteiligte:
    Cosmes Lopez, L.J. (Autor:in) / Arce, E. (Autor:in) / Torres, J. (Autor:in) / Vazquez-Arenas, J. (Autor:in) / Hallen, J.M. (Autor:in) / Cabrera-Sierra, R. (Autor:in)

    Erschienen in:

    Corrosion, Houston ; 67 , 11 ; 116001/1-116001/10


    Erscheinungsdatum :

    2011


    Format / Umfang :

    10 Seiten, 11 Bilder, 39 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Corrosion kinetics of pipeline carbon steel weld immersed in aqueous solution containing H2S

    Avendano-Castro, C. / Galvan-Martinez, R. / Contreras, A. et al. | Tema Archiv | 2009




    Simulating Cardiovascular Fluid Dynamics by the Immersed Boundary Method

    Griffith, B. / McQueen, D. / Peskin, C. et al. | British Library Conference Proceedings | 2009