In this case study, the failure cause of the tyre valves of trucks was investigated. Higher content sulphur and oxygen were detected by analyzing the corrosion products. The intergranular cracking morphologies were observed by SEM. The branch cracks were shown by metallographical and SEM observations. Residual stress was verified by hardness testing. Synthesizing all the experimental results the failed air valves were considered to be caused by sulphur dioxide SCC. The three necessary conditions for SCC were satisfied in this case study: susceptible brass alloy, corrosive media (SO2) contained in the surrounding environment, and sufficient tensile stress. In the end, some important suggestions were proposed to prevent the similar failures in the future.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Failure analysis of the tyre valves of trucks


    Beteiligte:
    Li, Yong-De (Autor:in) / Xu, Na (Autor:in) / Zhang, Li-Li (Autor:in) / Zhao, Mei (Autor:in) / Guo, Wei-min (Autor:in) / Yan, Guo-Gang (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2013


    Format / Umfang :

    7 Seiten, 10 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Tyre valves

    CHRISTOPHER FRAPPELL | Europäisches Patentamt | 2025

    Freier Zugriff

    TYRE VALVES

    FRAPPELL CHRISTOPHER | Europäisches Patentamt | 2025

    Freier Zugriff

    Tyre-changing machine for trucks

    MAGNANI FRANCO | Europäisches Patentamt | 2019

    Freier Zugriff

    TYRE-CHANGING MACHINE FOR TRUCKS

    MAGNANI FRANCO | Europäisches Patentamt | 2016

    Freier Zugriff

    Tyre-changing machine for trucks

    MAGNANI FRANCO | Europäisches Patentamt | 2016

    Freier Zugriff