The characteristics of DC butt welding of high strength hot rolled steel was studied in relation to the production of wheel rims. A thermal distribution analysis of DC butt welding indicated the importance of the optimization of welding condition as the maximum temperature attained in DC butt welding significantly differed from place to place along the welding line, Insufficient heat input or overheating might cause cold weld or solidification cracking. Particularly, the welding current and welding cycle should be strictly controlled in order to make a weld with good cold formability. The influence of steel chemistry on weld hardness was also investigated. High strength steel for DC butt rim welding should be produced with the least Ceq. because a relatively early stage bead trimming enhances lardenability of the weld, which increases sensitivity to cracking.
Application of high strength hot rolled steel to DC butt rim welding
Anwendung von hochfestem warmgewalzten Stahls für induktionsgeschweißte Felgen
SAE-Papers ; Mar ; 1-6
1990
6 Seiten, 13 Bilder, 1 Tabelle, 1 Quelle
Aufsatz (Konferenz)
Englisch
Application of high strength hot rolled steel to DC butt rim welding
Kraftfahrwesen | 1990
|BUTT WELDING STRUCTURE AND BUTT WELDING METHOD FOR EXTREMELY THICK STEEL PLATE
Europäisches Patentamt | 2016
|High-Strength, Hot-Rolled Steel Bars
SAE | 2003
Defects of joints of high-strength rails produced using flash-butt welding
Tema Archiv | 2013
|