An investigation was carried out in our laboratory to study the effect of the microstructure of nickel-aluminum-bronze (NAB) alloy on its cavitation corrosion behaviour in seawater using a 20-kHz ultrasonic induced cavitation facility. Cavitation tests were made under free corrosion conditions as a function of exposure time in natural seawater. Optical and scanning electron microscopy showed NAB immersed in stagnant seawater suffered from selective corrosion of the copper-rich alpha phase at boundaries with intermetallic kappa precipitates. The kappa precipitates and precipitate-free zones did not suffer corrosion. Cavitation made the surface of this alloy very rough, with large cavities or pits, ductile tearing and corrosion of the boundaries of the alpha columnar grains. In addition, the number of cavities and their size increased with exposure time. Microcracks 5-10 my m long were observed in the alpha phase adjacent to kappa precipitates along the cross-section of the material. Selective phase corrosion and cavitation stresses were considered to be the cause of the cracks observed.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    The role of microstructure of nickel-aluminium-bronze alloy on its cavitation corrosion behavior in natural seawater


    Beteiligte:
    Al-Hashem, A. (Autor:in) / Riad, W. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2002


    Format / Umfang :

    5 Seiten, 16 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch





    Exfoliation Corrosion Behavior of 2524 Aluminium Alloy

    Yang, S. / Yi, D. Q. / Yao, S. J. et al. | British Library Conference Proceedings | 2007


    Cavitation corrosion of nodular cast iron (NCI) in seawater - Microstructural effects

    Al-Hashem, A. / Abdullah, A. / Riad, W. | Tema Archiv | 2001


    Influence of microstructure on seawater corrosion of Al-Mg-Si alloy A6N01

    Takahashi, C. / Matsuoka, K. / Senda, T. et al. | Tema Archiv | 2000