Filament wound test specimens of glass fibre/polyester, glass fibre/epoxy, carbon fibre/epoxy and aramid fibre/epoxy composites have been simultaneously stored for two years under accelerated ageing conditions. Two climates were used, 40 deg C/80 percent RH and 60 deg C/80 percent RH respectively. The moisture absorption was registered by increase in weight of each test specimen. The effect of moisture and degradation on the mechanical properties has been studied and results from ILSS testes (ASTM D2344), NOL ring tests (ASTM D2290) and hydraulic bursting tests are presented and discussed.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Degradation of fibre composite pressure vessels during storage under accelerated ageing conditions


    Weitere Titelangaben:

    Chemischer Abbau von Faserverbundstoff-Druckgefäßen während der Lagerung unter beschleunigten Alterungsbedingungen


    Beteiligte:
    Kowalska, M. (Autor:in) / Danilsons, M. (Autor:in) / Helleday, E. (Autor:in)


    Erscheinungsdatum :

    1994


    Format / Umfang :

    5 Seiten, 2 Bilder, 8 Tabellen, 15 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Degradation of Fibre Composite Pressure Vessels during Storage under Accelerated Ageing Conditions

    Kowalska, M. / Danilsons, M. / Helleday, E. et al. | British Library Conference Proceedings | 1994


    Phosphorus deposition on a three-way catalyst under accelerated ageing conditions

    Benjamin, S F / Brogan, M / Collin, T et al. | SAGE Publications | 2012



    Phosphorus deposition on a three-way catalyst under accelerated ageing conditions

    Benjamin,S.F. / Brogan,M. / Collin,T. et al. | Kraftfahrwesen | 2012